Addition-cured high-temperature vulcanized silicone rubber chu hydrosilane addition reaction hmangin a thleng thei a ni. Heating condition hnuaiah chuan hydrogen-silicone oil awmna silane group leh methyl vinyl raw rubber-a vinyl group te chu chloroplatinic acid catalysis hnuaiah an react a, chu chuan cross-linking a siam a:
Addition-Cured High-Temperature Vulcanized silicone rubber chu single-component leh two-component type-ah then theih a ni. One-component addition-Cured High-Temperature Vulcanized silicone rubber hi tun dinhmunah chuan silicone rubber product chi khat a ni a, a lo thang chak hle a ni. Sulfidation inhibitor (as, etc.) a awm avangin a storage stability hi thla 2 atanga thla 12 thleng a ni thei. Extrusion atana hman rubber compound chu a tlangpuiin thla hnih chhung stably-a dah theih a ni a, molding rubber compound chu thla 12 vel chhung dah theih a ni bawk. -component addition -cured high-temperature vulcanized silicone rubber chu pakhat-component rubber aiin a rei zawk hle. Component pahnih mixing ratio chu 1:1 emaw 100:1.5 emaw a ni thei.
Rubber compound a mixing ratio 1:1 nei a component chu base rubber, crosslinking agent leh vulcanization inhibitor a ni a, B component erawh chu base rubber leh platinum catalyst a ni thung. 100:1.5 rubber compound ah chuan a component lian ber chu base rubber, crosslinking agent leh inhibitor te an ni a, surface component chu base rubber a ni a, catalytic agent dah belh a ni thung.
Addition-cured high high-temperature vulcanized silicone rubber thatna lian ber pakhat chu a shrinkage rate hi vulcanization process chhung hian a tlem hle a, chu chu NO-products chu curing reaction-ah a lo chhuak thin vang a ni. Mahse, curing reaction-ah chuan platinum catalyst hman a ngai a, chu chu hman laiin rimchhia thlen thei compound, nitrogen, phosphorus, leh sulfur ang chi element awmna compound, organic compound fast group nei, leh metal ion compound tin, lead, mercury, leh bismut te nen a inzawm tur a ni lo. Dik tak chuan, a châng chuan chutiang compound chu an thil siamah chuan inhibitor angin an dah belh a, chu chuan an storage stability a tichak a ni.